Marble PLA
WHAT IS MARBLE PLA?
Monocure 3D Marble PLA is easy to print filament which gives a very unique marble-like appearance once printed. A special combination of pigments and binding polymers help it to achieve that real marble look. Like all our filaments, this will not cause nozzle clogs or stringing.
PLA plastic or polylactic acid is a vegetable-based plastic material, which commonly uses cornstarch as a raw material. This material is a thermoplastic aliphatic polyester and it is the primary natural raw material used in 3D printing. PLA is a fully biodegradable thermoplastic polymer consisting of renewable raw materials. Among all 3D printing materials, PLA is one of the most popular materials used for additive manufacturing.
PHYSICAL PROPERTIES
Deflection Temperature Under Load (°C)
51.3 (Test Standard – ASTM D648-18)
Density (g/cm3)
1.24 (Test Standard – ASTM D792-13)
Tensile Strength (MPa)
46.9 (Test Standard – ISO 527-1:2012 / ISO 527-2:2012)
Nominal Tensile Strain at Break (%)
57 (Test Standard – ISO 527-1:2012 / ISO 527-2:2012)
Tensile Stress at Yield (MPa)
46.9 (Test Standard – ISO 527-1:2012 / ISO 527-2:2012)
Flexural Strength (MPa)
61.7 (Test Standard – ASTM D790-17)
Flexural Modulus (MPa)
2280 (Test Standard – ASTM D790-17)
Melt Mass Flow Rate (g/10min)
30.1 (Test Standard – ISO 1133-1:2011)
Notched Izod Impact (J/m)
108 (Test Standard – ASTM D256-10)
PRINTER SETTINGS
Spool Net Weight:
1kg
Diameter:
1.75mm ± 0.05mm
Print Temperature:
190-220°C
Print Speed:
50-110mm/s
APPLICATION & TIPS
Perfect for a very unique marble-like appearance.
For best results, the thinner the layer, the slower you print, the higher quality you will get.
PLA filament is an easy-to-use material that will print perfectly with a standard type of nozzle.
For good adhesion to the print bed and easy removal, we recommend installing a WHAM BAM Flexible Build System on your FDM Printer.